# | RUBBER | TEMPERATURE | TIME | JUDGEMENT METHOD |
---|---|---|---|---|
1 | (CR) | 100°C | 72Hours | Test the Hardness and Tensile Strength after Heat Aging |
2 | (NBR) | 100°C | 72Hours | Test the Hardness and Tensile Strength after Heat Aging |
# | RUBBER | TEMPERATURE | CONCENTRATION | TIME | JUDGEMENT METHOD |
---|---|---|---|---|---|
1 | (NBR) | 40°C | 50 PPHM | 72Hours | Visual after Ozone Testing |
2 | (CR) | 40°C | 200 PPHM | 72Hours | Visual after Ozone Testing |
3 | (NR) | 40°C | 200 PPHM | 72Hours | Visual after Ozone Testing |
# | RUBBER | TEMPERATURE | TIME | JUDGEMENT METHOD |
---|---|---|---|---|
1 | (CR) | -40°C / 120°C | 48Hours | Test the Hardness and Tensile Strength after Heat Aging |
2 | (NBR) | -30°C / 120°C | 48Hours | Visual after High-Low Temperature Testing |